Rare earth has a strong chemical affinity with impurities such as oxygen and sulfur in molten steel. At steelmaking temperature (about 1873K), rare earth can react with impurities such as oxygen and sulfur in molten steel to form rare earth oxides, sulfides or oxysulfides. The deoxidation equilibrium constant or desulfurization equilibrium constant of these reactions is lower than or close to that of commonly used deoxidizers and desulfurizers. Therefore, rare earth steel additives can be used as strong deoxidizers and desulfurizers for molten steel to purify it. Commonly used rare earth steel additives are mainly mixed rare earth metals or high-grade (RE>27%) aloion ferrosilicon daear prin, ac weithiau defnyddir ocsidau daear prin ag asiantau lleihau cymysg hefyd.
Gall ocsidau, sylffidau neu ocsisylfidau a gynhyrchir gan adwaith pridd prin ag ocsigen a sylffwr mewn dur tawdd aros yn rhannol yn y dur tawdd a dod yn gynhwysiant yn y dur. Oherwydd pwynt toddi uchel y cynhwysiadau hyn, gallant wasanaethu fel canolfannau cnewyllol anhomogenaidd pan fydd y dur tawdd yn cadarnhau, a chwarae rhan mewn mireinio strwythur solidification y dur; ac oherwydd nad yw'r cynhwysiadau hyn yn cael eu dadffurfio'n hawdd ar y tymheredd treigl, maent yn dal i gynnal siâp sfferig neu werthyd bach, fel y gellir rheoli morffoleg y cynhwysiant yn y dur, a thrwy hynny osgoi neu oresgyn anisotropi eiddo dur a achosir gan yr estyniad a dadffurfiad mathau eraill o gynhwysiant (fel MnS) yn ystod prosesu pwysedd poeth, a gwneud cyfarwyddiadau hydredol, traws a thrwch yr eiddo dur yn tueddu i fod yn gyson. Ar hyn o bryd y math hwn o addasiad o ddur prin wedi'i drin â daear yw'r cynnwys cymhwysiad pwysicaf o ychwanegion dur daear prin.