L{0}}PSL1 Cyfansoddiad cemegol (%)
| cyfansoddiad | C | Mn | P | S | Cr | Ni | Cu | Mo | B | Mwy | |
|---|---|---|---|---|---|---|---|---|---|---|---|
| Pibell Ddi-dor | Minnau | - | - | - | - | - | - | - | - | - | Nb+V+Ti Llai na neu'n hafal i 0.15 |
| Max | 0.28 | 1.4 | 0.03 | 0.03 | 0.5 | 0.5 | 0.5 | 0.15 | 0.001 |
| cyfansoddiad | C | Mn | P | S | Cr | Ni | Cu | Mo | B | Mwy | |
|---|---|---|---|---|---|---|---|---|---|---|---|
| Pibell wedi'i Weldio | Minnau | - | - | - | - | - | - | - | - | - | Nb+V+Ti Llai na neu'n hafal i 0.15 |
| Max | 0.26 | 1.45 | 0.03 | 0.03 | 0.5 | 0.5 | 0.5 | 0.15 | 0.001 |
L450-PSL1 Priodweddau mecanyddol
| Math | Cryfder Tynnol σb Mpa |
Pwynt Cynnyrch σs Mpa |
Elongation ar egwyl neu elongation δ % |
|---|---|---|---|
| Di-dor / Wedi'i Weldio | Yn fwy na neu'n hafal i 535 | Yn fwy na neu'n hafal i 450 |
L450Q-PSL2 Cyfansoddiad cemegol (%)
| cyfansoddiad | C | Si | Mn | P | S | Cr | Ni | Cu | Mo | B | Mwy | |
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Pibell Ddi-dor/Wedi'i Weldio | Minnau | - | - | - | - | - | - | - | - | - | - | Nb+V+Ti Llai na neu'n hafal i 0.15 |
| Max | 0.18 | 0.45 | 1.7 | 0.025 | 0.015 | 0.5 | 0.5 | 0.5 | 0.5 | 0.001 |
Priodweddau mecanyddol L450Q-PSL2
| Math | Tymheredd Prawf | Cryfder Tynnol σb Mpa |
Pwynt Cynnyrch σs |
Elongation ar egwyl neu elongation δ |
Sioc amsugno egni |
|---|---|---|---|---|---|
| Di-dor / Wedi'i Weldio | 535~760 | 450~600 | |||
| OD Llai na neu'n hafal i 30 | 0 gradd | Yn fwy na neu'n hafal i 27 | |||
| OD>30~48 | 0 gradd | Yn fwy na neu'n hafal i 40 | |||
| OD>48~84 | 0 gradd | Yn fwy na neu'n hafal i 54 |
L450M-PSL2 Cyfansoddiad cemegol (%)
| Cyfansoddiad | C | Si | Mn | P | S | Cr | Ni | Cu | Mo | B | Mwy | |
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Wedi'i Weldio | Minnau | - | - | - | - | - | - | - | - | - | - | Nb+V+Ti Llai na neu'n hafal i 0.15 |
| Max | 0.18 | 0.45 | 1.6 | 0.025 | 0.015 | 0.5 | 0.5 | 0.5 | 0.5 | 0.001 |