ASTM A209, Manyleb Safonol ar gyfer Boeler Aloi-Dur Carbon-Molybdenwm Di-dor a thiwbiau superheater.
OD: 10mm ~ 203mm
WT: 2.0mm~25mm
Hyd: 5.8-12m neu fel cwsmeriaid gofynnol
Gradd: ASTM A209 T1, ASTM A209 T1a, ASTM A209 T1b
Techneg: Di-dor
Defnydd:
1. Piblinell cludo hylif pwysedd isel a chanolig
2. gwaith pŵer
3. tiwb boeler
4. diwydiant petrocemegol
Pecyn: Arwyneb wedi'i drochi mewn olew neu wedi'i baentio'n ddu, wedi'i bacio mewn bagiau addas i'r môr, wedi'u bwndelu hecsagonol.
Cyfansoddiad Cemegol:
|
C |
Mn |
P |
S |
Os |
Mo |
|
|
T1 |
0.10-0.20 |
0.30-0.80 |
=0.025 |
=0.025 |
0.10-0.50 |
0.44-0.65 |
|
T1a |
0.15-0.25 |
0.30-0.80 |
=0.025 |
=0.025 |
0.10-0.50 |
0.44-0.65 |
|
T1b |
=0.14 |
0.30-0.80 |
=0.025 |
=0.025 |
0.10-0.50 |
0.44-0.65 |
Priodweddau Mecanyddol:
|
Gradd |
T1 |
T1a |
T1b |
|
Cryfder Tynnol Isafswm Ksi(Mpa) |
55(380) |
60(415) |
43(365) |
|
Cryfder Cynnyrch Isafswm Ksi(Mpa) |
30(205 |
32(220) |
28(195) |
|
Elongation mewn 2in neu 50mm min% |
30 |
30 |
30 |
Triniaeth wres:
A ddylai pibellau sydd wedi'u prosesu'n boeth ac wedi'u prosesu'n oer gael eu trin â gwres ar dymheredd o 650 gradd? O leiaf. Gall y gwneuthurwr ddewis anelio cyflawn, anelio isothermol neu normaleiddio ynghyd â thymeru. Ni ddylai'r tymheredd tymheru lleiaf fod yn is na 650 gradd.